Product range
| GS-procedure | Coating thickness | max. component size |
| Anodized natural (max. weight 4000 kg) | 5 – 25 μm | 4200 x 500 x 2600 mm |
| Anodized black (max. weight 750 kg) | 10 – 25 μm | 3000 x 500 x 1500 mm |
| GS-procedure | Coating thickness | max. component size |
| Blue, Gold, Gray, Red, Purple (max. weight 500 kg) | 10 – 25 μm | 900 x 400 x 900 mm |
| Other colors on Request |
| GSX-procedure | Coating thickness | max. component size |
| Hard anodizing (max. weight 4000 kg) | 20 – 100 μm | 4200 x 500 x 2600 mm |
| Hard anodizing black (max. weight 750 kg) | 20 – 100 μm | 3000 x 500 x 1500 mm |
| Bengough-Stuart Procedure | Coating thickness | max. component size |
| Chromic acid Eloxal (max. weight 100 kg) | 1 – 6 μm | 1800 x 500 x 900 mm |
| Yellow chromate with ALODINE 1200 | Coating thickness | max. component size |
| Chemical oxidation (max. weight 100 kg) | — | 900 x 500 x 900 mm |
| Passivate with Surtec 650 | Coating thickness | max. component size |
| Al – passivate (max. weight 750 kg) | — | 3000 x 500 x 1500 mm |
| Electroless Nickel Optic Special processes for UP – processing | Coating thickness | max. component size |
| Electroless Nickel (max. weight 3000 kg) | 5 – 100 μm | 2100 x 450 x 1600 mm |
| High performance bath for a wide field of application | Coating thickness | max. component size |
| Hard chrome(max. weight 250 kg) | 5 – 100 μm | 1000 x 500 x 900 mm |
| Alkaline process with colorless passivation as a substitute for the Cadmium plating process | Coating thickness | max. component size |
| Zinc-Nickel (max. weight 100 kg) | 5 – 30 μm | 900 x 500 x 900 mm |
| Sulfuric acid process for glossy, fine-grained and ductile coatings | Coating thickness | max. component size |
| Copper plating (max. weight 100 kg) | 5 – 100 μm | 500 x 300 x 300 mm |
| AMS method 1 type 1-8 ASTM typ 1-5 LAT4-1201 type A, B and D LN 9368-1201 | Coating thickness | max. component size |
| stainless steel passivate (max. weight 500 kg) | — | 500 x 300 x 300 mm |
| Eddy current method |
| Micro hardness in Vickers hardness |
| XRAY-process |
| Metal grinding |
| Electrical resistance test according to MIL |
| Corrosion test with 2 Salt spray chambers |
| Certified according to EN 9100 |